Coefficient of friction and wear of sputtered a-C thin coatings containing Mo

Petr Novák, J. Musil, R. Čerstvỳ, A. Jäger

Результат исследований: Материалы для журналаСтатья

11 Цитирования (Scopus)

Аннотация

The paper reports on preparation of ~3000nm thick a-C coatings containing Mo, interrelationships between their mechanical properties, a coefficient of friction μ and wear rate k and the effect of Mo content in the a-C coating on these interrelationships. The Mo-C coatings were prepared by sputtering using an unbalanced magnetron (UM) equipped with a graphite targets (Ø=100mm, 99.9% purity) fixed to the UM cathode with Mo ring of different inner diameter Ø i. The content of Mo in the a-C coating was controlled by Ø i. It is shown that μ and k of the coating strongly depend not only on its hardness H but also on its effective Young's modulus E *=E/(1-ν 2), the ratios H/E *, H 3/E *2 and the elastic recovery W e; here E is the Young's modulus and ν is the Poisson ratio. The ratio H 3/E *2 characterizes the resistance of coating to plastic deformation. Coatings with a low amount of Mo composed of nanograins of carbides dispersed in a-C matrix exhibit low values of μ≈0.07 and k≈10 -7mm 3/Nm measured with WC ball at the rotation speed v=0.05m/s, total sliding length l=1000m and the load L=2N.

Язык оригиналаАнглийский
Страницы (с-по)1486-1490
Число страниц5
ЖурналSurface and Coatings Technology
Том205
Номер выпуска5
DOI
СостояниеОпубликовано - 25 ноя 2010

ASJC Scopus subject areas

  • Chemistry(all)
  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

Fingerprint Подробные сведения о темах исследования «Coefficient of friction and wear of sputtered a-C thin coatings containing Mo». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать