Characterization of ternary C-Si-Al nanocomposite thin films obtained by TVA method

C. Porosnicu, C. P. Lungu, I. Jepu, O. G. Pompilian, P. Dinca, C. Luculescu, G. Prodan, A. Marin, A. Vladescu, R. Vladoiu

Результат исследований: Материалы для журналаСтатья

Выдержка

Thin film depositions on certain substrates can improve or diminish the physical-chemical behavior of the coated material. For the present work there were used three basic elements: C, Si and Al as coating materials on glass, silicon and OLC45 steel substrates. The purpose of the research is to obtain an optimum combination for properties' improvement, as hardness, adherence and low friction. Nevertheless, such special characteristics can be found likely in a composite material. Ternary C-Si-Al samples of 1 micron thickness were successfully obtained for the first time using Thermionic Vacuum Arc (TVA) deposition method. Depth profile measurements confirmed both the thickness of the obtained layer and the high roughness of the layers deposited on OLC 45 steel substrate. The granular structure of the films was pointed out by SEM, AFM and TEM measurements. XPS measurements highlighted the formation of aluminum and silicon oxides due to the layer exposure to the residual gas existent in the deposition chamber. The friction coefficient of the coatings was two or three times lower in comparison with the one of the uncoated substrates. Film hardness was found to be high with values between 3600 and 5000N/mm2 (~3.6-5.0 GPa), depending on the penetration depth.

Язык оригиналаАнглийский
Страницы (с-по)765-775
Число страниц11
ЖурналDigest Journal of Nanomaterials and Biostructures
Том9
Номер выпуска2
СостояниеОпубликовано - 1 янв 2014
Опубликовано для внешнего пользованияДа

Отпечаток

Nanocomposites
Nanocomposite films
thermionics
Friction
Steel
Hardness
Silicon
Vacuum
nanocomposites
arcs
Thin films
vacuum
Aluminum Oxide
Substrates
thin films
Glass
hardness
Gases
steels
Coated materials

ASJC Scopus subject areas

  • Structural Biology
  • Atomic and Molecular Physics, and Optics
  • Biomedical Engineering
  • Materials Science(all)
  • Condensed Matter Physics
  • Physical and Theoretical Chemistry

Цитировать

Porosnicu, C., Lungu, C. P., Jepu, I., Pompilian, O. G., Dinca, P., Luculescu, C., ... Vladoiu, R. (2014). Characterization of ternary C-Si-Al nanocomposite thin films obtained by TVA method. Digest Journal of Nanomaterials and Biostructures, 9(2), 765-775.

Characterization of ternary C-Si-Al nanocomposite thin films obtained by TVA method. / Porosnicu, C.; Lungu, C. P.; Jepu, I.; Pompilian, O. G.; Dinca, P.; Luculescu, C.; Prodan, G.; Marin, A.; Vladescu, A.; Vladoiu, R.

В: Digest Journal of Nanomaterials and Biostructures, Том 9, № 2, 01.01.2014, стр. 765-775.

Результат исследований: Материалы для журналаСтатья

Porosnicu, C, Lungu, CP, Jepu, I, Pompilian, OG, Dinca, P, Luculescu, C, Prodan, G, Marin, A, Vladescu, A & Vladoiu, R 2014, 'Characterization of ternary C-Si-Al nanocomposite thin films obtained by TVA method', Digest Journal of Nanomaterials and Biostructures, том. 9, № 2, стр. 765-775.
Porosnicu C, Lungu CP, Jepu I, Pompilian OG, Dinca P, Luculescu C и соавт. Characterization of ternary C-Si-Al nanocomposite thin films obtained by TVA method. Digest Journal of Nanomaterials and Biostructures. 2014 Янв. 1;9(2):765-775.
Porosnicu, C. ; Lungu, C. P. ; Jepu, I. ; Pompilian, O. G. ; Dinca, P. ; Luculescu, C. ; Prodan, G. ; Marin, A. ; Vladescu, A. ; Vladoiu, R. / Characterization of ternary C-Si-Al nanocomposite thin films obtained by TVA method. В: Digest Journal of Nanomaterials and Biostructures. 2014 ; Том 9, № 2. стр. 765-775.
@article{00b270a18fa14e47b4eda6bbc8b89cee,
title = "Characterization of ternary C-Si-Al nanocomposite thin films obtained by TVA method",
abstract = "Thin film depositions on certain substrates can improve or diminish the physical-chemical behavior of the coated material. For the present work there were used three basic elements: C, Si and Al as coating materials on glass, silicon and OLC45 steel substrates. The purpose of the research is to obtain an optimum combination for properties' improvement, as hardness, adherence and low friction. Nevertheless, such special characteristics can be found likely in a composite material. Ternary C-Si-Al samples of 1 micron thickness were successfully obtained for the first time using Thermionic Vacuum Arc (TVA) deposition method. Depth profile measurements confirmed both the thickness of the obtained layer and the high roughness of the layers deposited on OLC 45 steel substrate. The granular structure of the films was pointed out by SEM, AFM and TEM measurements. XPS measurements highlighted the formation of aluminum and silicon oxides due to the layer exposure to the residual gas existent in the deposition chamber. The friction coefficient of the coatings was two or three times lower in comparison with the one of the uncoated substrates. Film hardness was found to be high with values between 3600 and 5000N/mm2 (~3.6-5.0 GPa), depending on the penetration depth.",
keywords = "Carbon nanocomposites, Coating materials, Dry sliding, Low-friction, TVA",
author = "C. Porosnicu and Lungu, {C. P.} and I. Jepu and Pompilian, {O. G.} and P. Dinca and C. Luculescu and G. Prodan and A. Marin and A. Vladescu and R. Vladoiu",
year = "2014",
month = "1",
day = "1",
language = "English",
volume = "9",
pages = "765--775",
journal = "Digest Journal of Nanomaterials and Biostructures",
issn = "1842-3582",
publisher = "National Institute R and D of Materials Physics",
number = "2",

}

TY - JOUR

T1 - Characterization of ternary C-Si-Al nanocomposite thin films obtained by TVA method

AU - Porosnicu, C.

AU - Lungu, C. P.

AU - Jepu, I.

AU - Pompilian, O. G.

AU - Dinca, P.

AU - Luculescu, C.

AU - Prodan, G.

AU - Marin, A.

AU - Vladescu, A.

AU - Vladoiu, R.

PY - 2014/1/1

Y1 - 2014/1/1

N2 - Thin film depositions on certain substrates can improve or diminish the physical-chemical behavior of the coated material. For the present work there were used three basic elements: C, Si and Al as coating materials on glass, silicon and OLC45 steel substrates. The purpose of the research is to obtain an optimum combination for properties' improvement, as hardness, adherence and low friction. Nevertheless, such special characteristics can be found likely in a composite material. Ternary C-Si-Al samples of 1 micron thickness were successfully obtained for the first time using Thermionic Vacuum Arc (TVA) deposition method. Depth profile measurements confirmed both the thickness of the obtained layer and the high roughness of the layers deposited on OLC 45 steel substrate. The granular structure of the films was pointed out by SEM, AFM and TEM measurements. XPS measurements highlighted the formation of aluminum and silicon oxides due to the layer exposure to the residual gas existent in the deposition chamber. The friction coefficient of the coatings was two or three times lower in comparison with the one of the uncoated substrates. Film hardness was found to be high with values between 3600 and 5000N/mm2 (~3.6-5.0 GPa), depending on the penetration depth.

AB - Thin film depositions on certain substrates can improve or diminish the physical-chemical behavior of the coated material. For the present work there were used three basic elements: C, Si and Al as coating materials on glass, silicon and OLC45 steel substrates. The purpose of the research is to obtain an optimum combination for properties' improvement, as hardness, adherence and low friction. Nevertheless, such special characteristics can be found likely in a composite material. Ternary C-Si-Al samples of 1 micron thickness were successfully obtained for the first time using Thermionic Vacuum Arc (TVA) deposition method. Depth profile measurements confirmed both the thickness of the obtained layer and the high roughness of the layers deposited on OLC 45 steel substrate. The granular structure of the films was pointed out by SEM, AFM and TEM measurements. XPS measurements highlighted the formation of aluminum and silicon oxides due to the layer exposure to the residual gas existent in the deposition chamber. The friction coefficient of the coatings was two or three times lower in comparison with the one of the uncoated substrates. Film hardness was found to be high with values between 3600 and 5000N/mm2 (~3.6-5.0 GPa), depending on the penetration depth.

KW - Carbon nanocomposites

KW - Coating materials

KW - Dry sliding

KW - Low-friction

KW - TVA

UR - http://www.scopus.com/inward/record.url?scp=84901750600&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84901750600&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:84901750600

VL - 9

SP - 765

EP - 775

JO - Digest Journal of Nanomaterials and Biostructures

JF - Digest Journal of Nanomaterials and Biostructures

SN - 1842-3582

IS - 2

ER -