Characterization of multi-principal-element (TiZrNbHfTa)N and (TiZrNbHfTa)C coatings for biomedical applications

V. Braic, M. Balaceanu, M. Braic, A. Vladescu, S. Panseri, A. Russo

Результат исследований: Материалы для журналаСтатья

74 Цитирования (Scopus)

Аннотация

Multi-principal-element (TiZrNbHfTa)N and (TiZrNbHfTa)C coatings were deposited on Ti6Al4V alloy by co-sputtering of Ti, Zr, Nb, Hf and Ta metallic targets in reactive atmosphere. The coatings were analyzed for elemental and phase compositions, crystalline structure, morphology, residual stress, hardness, friction performance, wear-corrosion resistance and cell viability. For all the films, only simple fcc solid solutions with (111) preferred orientations were found, with crystallite sizes in the range 7.2-13.5nm. The coatings were subjected to compressive stress, with values ranging from 0.8 to 1.6GPa. The carbide coating with the highest carbon content (carbon/metal ≈1.3) exhibited the highest hardness of about 31 GPa, the best friction behavior (μ = 0.12) and the highest wear resistance (wear rate K=0.2×10 -6mm 3N -1m -1), when testing in simulated body fluids (SBFs). Cell viability tests proved that the osteoblast cells were adherent to the coated substrates, and a very high percentage of live cells were observed on sample surfaces, after 72h incubation time.

Язык оригиналаАнглийский
Страницы (с-по)197-205
Число страниц9
ЖурналJournal of the Mechanical Behavior of Biomedical Materials
Том10
DOI
СостояниеОпубликовано - 1 июн 2012
Опубликовано для внешнего пользованияДа

    Fingerprint

ASJC Scopus subject areas

  • Biomaterials
  • Biomedical Engineering
  • Mechanics of Materials

Цитировать