By means of electron-positron annihilation method, defects formation in titanium under electrolytic hydrogen charging from LiOH + H2O solution has been studied. Effects of thermal annealing and electron irradiation on defect structure of hydrogen-containing titanium were investigated. Mean positron lifetime and F-parameter were found to be decreased after electron irradiation of hydrogen-charged specimens. Effects observed are connected with defect structure modification induced by rapid hydrogen migration and defects annihilation.
|Журнал||Fizika i Khimiya Obrabotki Materialov|
|Состояние||Опубликовано - 2002|