The microstructure of aluminum-magnesium alloy friction stir weld

Olga Sizova, Alexander Kolubaev, Evgeny Alexangrovich Kolubaev, Anastasiya Zaikina, Valery Evgenievich Rubtsov, Sergey Psakhie, Alexander Chernyavsky, Vitaly Lopota

Research output: Chapter in Book/Report/Conference proceedingConference contribution

2 Citations (Scopus)

Abstract

Friction stir weld joint of aluminum/magnesium alloy has been structurally characterized after tensile testing. A butt-weld flaw which a surface of joining between two sheets has been revealed. This defect dictates the specificity of sample's fracture in a tensile test.

Original languageEnglish
Title of host publicationAIP Conference Proceedings
PublisherAmerican Institute of Physics Inc.
Pages587-590
Number of pages4
Volume1623
ISBN (Print)9780735412606
DOIs
Publication statusPublished - 2014
EventInternational Conference on Physical Mesomechanics of Multilevel Systems 2014 - Tomsk, Russian Federation
Duration: 3 Sep 20145 Sep 2014

Other

OtherInternational Conference on Physical Mesomechanics of Multilevel Systems 2014
CountryRussian Federation
CityTomsk
Period3.9.145.9.14

Fingerprint

magnesium alloys
aluminum alloys
friction
microstructure
defects
tensile tests

Keywords

  • Aluminum-magnesium alloy
  • Failure
  • Friction stir welding
  • Microstructure
  • Weld

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Cite this

Sizova, O., Kolubaev, A., Kolubaev, E. A., Zaikina, A., Rubtsov, VE., Psakhie, S., ... Lopota, V. (2014). The microstructure of aluminum-magnesium alloy friction stir weld. In AIP Conference Proceedings (Vol. 1623, pp. 587-590). American Institute of Physics Inc.. https://doi.org/10.1063/1.4899013

The microstructure of aluminum-magnesium alloy friction stir weld. / Sizova, Olga; Kolubaev, Alexander; Kolubaev, Evgeny Alexangrovich; Zaikina, Anastasiya; Rubtsov, Valery Evgenievich; Psakhie, Sergey; Chernyavsky, Alexander; Lopota, Vitaly.

AIP Conference Proceedings. Vol. 1623 American Institute of Physics Inc., 2014. p. 587-590.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Sizova, O, Kolubaev, A, Kolubaev, EA, Zaikina, A, Rubtsov, VE, Psakhie, S, Chernyavsky, A & Lopota, V 2014, The microstructure of aluminum-magnesium alloy friction stir weld. in AIP Conference Proceedings. vol. 1623, American Institute of Physics Inc., pp. 587-590, International Conference on Physical Mesomechanics of Multilevel Systems 2014, Tomsk, Russian Federation, 3.9.14. https://doi.org/10.1063/1.4899013
Sizova O, Kolubaev A, Kolubaev EA, Zaikina A, Rubtsov VE, Psakhie S et al. The microstructure of aluminum-magnesium alloy friction stir weld. In AIP Conference Proceedings. Vol. 1623. American Institute of Physics Inc. 2014. p. 587-590 https://doi.org/10.1063/1.4899013
Sizova, Olga ; Kolubaev, Alexander ; Kolubaev, Evgeny Alexangrovich ; Zaikina, Anastasiya ; Rubtsov, Valery Evgenievich ; Psakhie, Sergey ; Chernyavsky, Alexander ; Lopota, Vitaly. / The microstructure of aluminum-magnesium alloy friction stir weld. AIP Conference Proceedings. Vol. 1623 American Institute of Physics Inc., 2014. pp. 587-590
@inproceedings{904087301e844e888494e6bebcc002ed,
title = "The microstructure of aluminum-magnesium alloy friction stir weld",
abstract = "Friction stir weld joint of aluminum/magnesium alloy has been structurally characterized after tensile testing. A butt-weld flaw which a surface of joining between two sheets has been revealed. This defect dictates the specificity of sample's fracture in a tensile test.",
keywords = "Aluminum-magnesium alloy, Failure, Friction stir welding, Microstructure, Weld",
author = "Olga Sizova and Alexander Kolubaev and Kolubaev, {Evgeny Alexangrovich} and Anastasiya Zaikina and Valery Evgenievich Rubtsov and Sergey Psakhie and Alexander Chernyavsky and Vitaly Lopota",
year = "2014",
doi = "10.1063/1.4899013",
language = "English",
isbn = "9780735412606",
volume = "1623",
pages = "587--590",
booktitle = "AIP Conference Proceedings",
publisher = "American Institute of Physics Inc.",

}

TY - GEN

T1 - The microstructure of aluminum-magnesium alloy friction stir weld

AU - Sizova, Olga

AU - Kolubaev, Alexander

AU - Kolubaev, Evgeny Alexangrovich

AU - Zaikina, Anastasiya

AU - Rubtsov, Valery Evgenievich

AU - Psakhie, Sergey

AU - Chernyavsky, Alexander

AU - Lopota, Vitaly

PY - 2014

Y1 - 2014

N2 - Friction stir weld joint of aluminum/magnesium alloy has been structurally characterized after tensile testing. A butt-weld flaw which a surface of joining between two sheets has been revealed. This defect dictates the specificity of sample's fracture in a tensile test.

AB - Friction stir weld joint of aluminum/magnesium alloy has been structurally characterized after tensile testing. A butt-weld flaw which a surface of joining between two sheets has been revealed. This defect dictates the specificity of sample's fracture in a tensile test.

KW - Aluminum-magnesium alloy

KW - Failure

KW - Friction stir welding

KW - Microstructure

KW - Weld

UR - http://www.scopus.com/inward/record.url?scp=84915749697&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84915749697&partnerID=8YFLogxK

U2 - 10.1063/1.4899013

DO - 10.1063/1.4899013

M3 - Conference contribution

SN - 9780735412606

VL - 1623

SP - 587

EP - 590

BT - AIP Conference Proceedings

PB - American Institute of Physics Inc.

ER -