Synthesis of bimetallic AuPt/CeO2 catalysts and their comparative study in CO oxidation under different reaction conditions

Pavel E. Plyusnin, Elena M. Slavinskaya, Roman M. Kenzhin, Anastasiya K. Kirilovich, Evgeniya V. Makotchenko, Olga A. Stonkus, Yury V. Shubin, Aleksey A. Vedyagin

Research output: Contribution to journalArticle

3 Citations (Scopus)

Abstract

In the present work, ceria-supported Au–Pt catalyst with metal ratio 3:2 was prepared using a “single-source precursor” concept. The double complex salt [AuEn2]2[Pt(NO2)4]3·6H2O was used as such precursor. CeO2 of unique morphology with developed surface area (120 m2/g) obtained by urea precipitation technique was used as a support. According to XRD data, size of the alloyed Au–Pt particles was estimated to be less than 3 nm. It was shown that bimetallic Au–Pt system intensifies release of oxygen from the CeO2 lattice. The 0.5%Au2Pt3/CeO2 catalyst was comparatively studied in low temperature CO oxidation (simplified model reaction mixture) and under prompt thermal aging conditions (complex reaction mixture) with regard to monometallic reference samples 0.2%Au/CeO2 and 0.3%Pt/CeO2. The catalytic performance of the samples was found to be significantly dependent on the reaction and pre-treatment conditions. In the case of the bimetallic catalyst, reversible redistribution and enrichment of the nanoparticle surface with Pt or Au were shown to be the key factor defining the activity.

Original languageEnglish
JournalReaction Kinetics, Mechanisms and Catalysis
DOIs
Publication statusPublished - 1 Jan 2019

Fingerprint

Carbon Monoxide
catalysts
Oxidation
oxidation
Catalysts
Thermal aging
Cerium compounds
synthesis
Catalyst supports
Urea
Salts
Metals
Oxygen
Nanoparticles
ureas
pretreatment
salts
nanoparticles
oxygen
metals

Keywords

  • Bimetallic AuPt alloys
  • CO oxidation
  • Double complex salt
  • Preparation
  • Thermal stability

ASJC Scopus subject areas

  • Catalysis
  • Physical and Theoretical Chemistry

Cite this

Synthesis of bimetallic AuPt/CeO2 catalysts and their comparative study in CO oxidation under different reaction conditions. / Plyusnin, Pavel E.; Slavinskaya, Elena M.; Kenzhin, Roman M.; Kirilovich, Anastasiya K.; Makotchenko, Evgeniya V.; Stonkus, Olga A.; Shubin, Yury V.; Vedyagin, Aleksey A.

In: Reaction Kinetics, Mechanisms and Catalysis, 01.01.2019.

Research output: Contribution to journalArticle

Plyusnin, Pavel E. ; Slavinskaya, Elena M. ; Kenzhin, Roman M. ; Kirilovich, Anastasiya K. ; Makotchenko, Evgeniya V. ; Stonkus, Olga A. ; Shubin, Yury V. ; Vedyagin, Aleksey A. / Synthesis of bimetallic AuPt/CeO2 catalysts and their comparative study in CO oxidation under different reaction conditions. In: Reaction Kinetics, Mechanisms and Catalysis. 2019.
@article{a74119e8cf6549a8bccf62527286f184,
title = "Synthesis of bimetallic AuPt/CeO2 catalysts and their comparative study in CO oxidation under different reaction conditions",
abstract = "In the present work, ceria-supported Au–Pt catalyst with metal ratio 3:2 was prepared using a “single-source precursor” concept. The double complex salt [AuEn2]2[Pt(NO2)4]3·6H2O was used as such precursor. CeO2 of unique morphology with developed surface area (120 m2/g) obtained by urea precipitation technique was used as a support. According to XRD data, size of the alloyed Au–Pt particles was estimated to be less than 3 nm. It was shown that bimetallic Au–Pt system intensifies release of oxygen from the CeO2 lattice. The 0.5{\%}Au2Pt3/CeO2 catalyst was comparatively studied in low temperature CO oxidation (simplified model reaction mixture) and under prompt thermal aging conditions (complex reaction mixture) with regard to monometallic reference samples 0.2{\%}Au/CeO2 and 0.3{\%}Pt/CeO2. The catalytic performance of the samples was found to be significantly dependent on the reaction and pre-treatment conditions. In the case of the bimetallic catalyst, reversible redistribution and enrichment of the nanoparticle surface with Pt or Au were shown to be the key factor defining the activity.",
keywords = "Bimetallic AuPt alloys, CO oxidation, Double complex salt, Preparation, Thermal stability",
author = "Plyusnin, {Pavel E.} and Slavinskaya, {Elena M.} and Kenzhin, {Roman M.} and Kirilovich, {Anastasiya K.} and Makotchenko, {Evgeniya V.} and Stonkus, {Olga A.} and Shubin, {Yury V.} and Vedyagin, {Aleksey A.}",
year = "2019",
month = "1",
day = "1",
doi = "10.1007/s11144-019-01545-5",
language = "English",
journal = "Reaction Kinetics, Mechanisms and Catalysis",
issn = "1878-5190",
publisher = "Springer Netherlands",

}

TY - JOUR

T1 - Synthesis of bimetallic AuPt/CeO2 catalysts and their comparative study in CO oxidation under different reaction conditions

AU - Plyusnin, Pavel E.

AU - Slavinskaya, Elena M.

AU - Kenzhin, Roman M.

AU - Kirilovich, Anastasiya K.

AU - Makotchenko, Evgeniya V.

AU - Stonkus, Olga A.

AU - Shubin, Yury V.

AU - Vedyagin, Aleksey A.

PY - 2019/1/1

Y1 - 2019/1/1

N2 - In the present work, ceria-supported Au–Pt catalyst with metal ratio 3:2 was prepared using a “single-source precursor” concept. The double complex salt [AuEn2]2[Pt(NO2)4]3·6H2O was used as such precursor. CeO2 of unique morphology with developed surface area (120 m2/g) obtained by urea precipitation technique was used as a support. According to XRD data, size of the alloyed Au–Pt particles was estimated to be less than 3 nm. It was shown that bimetallic Au–Pt system intensifies release of oxygen from the CeO2 lattice. The 0.5%Au2Pt3/CeO2 catalyst was comparatively studied in low temperature CO oxidation (simplified model reaction mixture) and under prompt thermal aging conditions (complex reaction mixture) with regard to monometallic reference samples 0.2%Au/CeO2 and 0.3%Pt/CeO2. The catalytic performance of the samples was found to be significantly dependent on the reaction and pre-treatment conditions. In the case of the bimetallic catalyst, reversible redistribution and enrichment of the nanoparticle surface with Pt or Au were shown to be the key factor defining the activity.

AB - In the present work, ceria-supported Au–Pt catalyst with metal ratio 3:2 was prepared using a “single-source precursor” concept. The double complex salt [AuEn2]2[Pt(NO2)4]3·6H2O was used as such precursor. CeO2 of unique morphology with developed surface area (120 m2/g) obtained by urea precipitation technique was used as a support. According to XRD data, size of the alloyed Au–Pt particles was estimated to be less than 3 nm. It was shown that bimetallic Au–Pt system intensifies release of oxygen from the CeO2 lattice. The 0.5%Au2Pt3/CeO2 catalyst was comparatively studied in low temperature CO oxidation (simplified model reaction mixture) and under prompt thermal aging conditions (complex reaction mixture) with regard to monometallic reference samples 0.2%Au/CeO2 and 0.3%Pt/CeO2. The catalytic performance of the samples was found to be significantly dependent on the reaction and pre-treatment conditions. In the case of the bimetallic catalyst, reversible redistribution and enrichment of the nanoparticle surface with Pt or Au were shown to be the key factor defining the activity.

KW - Bimetallic AuPt alloys

KW - CO oxidation

KW - Double complex salt

KW - Preparation

KW - Thermal stability

UR - http://www.scopus.com/inward/record.url?scp=85060945255&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85060945255&partnerID=8YFLogxK

U2 - 10.1007/s11144-019-01545-5

DO - 10.1007/s11144-019-01545-5

M3 - Article

AN - SCOPUS:85060945255

JO - Reaction Kinetics, Mechanisms and Catalysis

JF - Reaction Kinetics, Mechanisms and Catalysis

SN - 1878-5190

ER -