Surface Modification of Corundum Ceramics by Argon Ion Beam

S. A. Ghyngazov, V. Kostenko, V. V. Ovchinnikov, N. V. Gushchina, F. F. Makhinko

Research output: Contribution to journalArticle

Abstract

Abstract: The mechanical properties of near-surface layers of aluminum oxide ceramic treated with a continuous ion beam of argon are investigated. The phase and structural changes of the modified near-surface layers were analyzed by X-ray diffraction analysis and scanning electron microscopy, respectively. Samples for research were made from corundum plates used in microelectronics. Ion processing was carried out using an ILM-1 ion implanter equipped with a Pulsar-1M ion source based on a low-pressure glow discharge with a cold hollow cathode. Argon ions with energy of 30 keV and ion current density j = 300 μA/cm2 were used for the irradiation. Two irradiation modes with the fluences of 1016 and 1017 cm–2 were implemented. It was established that the ion treatment promotes the manifestation of the initial grain structure of a sample and increases the mechanical characteristics (modulus of elasticity and nanohardness) of near-surface layers of samples. According to the X-ray diffraction data, after the action of an ion beam, there is a decrease in the size of the coherent scattering region with respect to the initial state. The irradiation leads to an increase in the values of crystal lattice microstrains. Possible mechanisms of modifying the ceramic surface are discussed.

Original languageEnglish
Pages (from-to)438-444
Number of pages7
JournalInorganic Materials: Applied Research
Volume10
Issue number2
DOIs
Publication statusPublished - 1 Mar 2019

Fingerprint

Corundum
Aluminum Oxide
Argon
Ion beams
Surface treatment
Ions
Irradiation
Nanohardness
Coherent scattering
DEAE-Dextran
Crystal microstructure
Glow discharges
Ion sources
Microelectronics
Crystal lattices
X ray diffraction analysis
Cathodes
Current density
Elastic moduli
Aluminum

Keywords

  • aluminum oxide ceramic (corundum)
  • ion beams
  • mechanical characteristics
  • X-ray phase analysis

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

Cite this

Surface Modification of Corundum Ceramics by Argon Ion Beam. / Ghyngazov, S. A.; Kostenko, V.; Ovchinnikov, V. V.; Gushchina, N. V.; Makhinko, F. F.

In: Inorganic Materials: Applied Research, Vol. 10, No. 2, 01.03.2019, p. 438-444.

Research output: Contribution to journalArticle

Ghyngazov, S. A. ; Kostenko, V. ; Ovchinnikov, V. V. ; Gushchina, N. V. ; Makhinko, F. F. / Surface Modification of Corundum Ceramics by Argon Ion Beam. In: Inorganic Materials: Applied Research. 2019 ; Vol. 10, No. 2. pp. 438-444.
@article{cea0f8bc2b944db3bc38bcd9ca43cdd9,
title = "Surface Modification of Corundum Ceramics by Argon Ion Beam",
abstract = "Abstract: The mechanical properties of near-surface layers of aluminum oxide ceramic treated with a continuous ion beam of argon are investigated. The phase and structural changes of the modified near-surface layers were analyzed by X-ray diffraction analysis and scanning electron microscopy, respectively. Samples for research were made from corundum plates used in microelectronics. Ion processing was carried out using an ILM-1 ion implanter equipped with a Pulsar-1M ion source based on a low-pressure glow discharge with a cold hollow cathode. Argon ions with energy of 30 keV and ion current density j = 300 μA/cm2 were used for the irradiation. Two irradiation modes with the fluences of 1016 and 1017 cm–2 were implemented. It was established that the ion treatment promotes the manifestation of the initial grain structure of a sample and increases the mechanical characteristics (modulus of elasticity and nanohardness) of near-surface layers of samples. According to the X-ray diffraction data, after the action of an ion beam, there is a decrease in the size of the coherent scattering region with respect to the initial state. The irradiation leads to an increase in the values of crystal lattice microstrains. Possible mechanisms of modifying the ceramic surface are discussed.",
keywords = "aluminum oxide ceramic (corundum), ion beams, mechanical characteristics, X-ray phase analysis",
author = "Ghyngazov, {S. A.} and V. Kostenko and Ovchinnikov, {V. V.} and Gushchina, {N. V.} and Makhinko, {F. F.}",
year = "2019",
month = "3",
day = "1",
doi = "10.1134/S2075113319020199",
language = "English",
volume = "10",
pages = "438--444",
journal = "Inorganic Materials: Applied Research",
issn = "2075-1133",
publisher = "Springer Verlag",
number = "2",

}

TY - JOUR

T1 - Surface Modification of Corundum Ceramics by Argon Ion Beam

AU - Ghyngazov, S. A.

AU - Kostenko, V.

AU - Ovchinnikov, V. V.

AU - Gushchina, N. V.

AU - Makhinko, F. F.

PY - 2019/3/1

Y1 - 2019/3/1

N2 - Abstract: The mechanical properties of near-surface layers of aluminum oxide ceramic treated with a continuous ion beam of argon are investigated. The phase and structural changes of the modified near-surface layers were analyzed by X-ray diffraction analysis and scanning electron microscopy, respectively. Samples for research were made from corundum plates used in microelectronics. Ion processing was carried out using an ILM-1 ion implanter equipped with a Pulsar-1M ion source based on a low-pressure glow discharge with a cold hollow cathode. Argon ions with energy of 30 keV and ion current density j = 300 μA/cm2 were used for the irradiation. Two irradiation modes with the fluences of 1016 and 1017 cm–2 were implemented. It was established that the ion treatment promotes the manifestation of the initial grain structure of a sample and increases the mechanical characteristics (modulus of elasticity and nanohardness) of near-surface layers of samples. According to the X-ray diffraction data, after the action of an ion beam, there is a decrease in the size of the coherent scattering region with respect to the initial state. The irradiation leads to an increase in the values of crystal lattice microstrains. Possible mechanisms of modifying the ceramic surface are discussed.

AB - Abstract: The mechanical properties of near-surface layers of aluminum oxide ceramic treated with a continuous ion beam of argon are investigated. The phase and structural changes of the modified near-surface layers were analyzed by X-ray diffraction analysis and scanning electron microscopy, respectively. Samples for research were made from corundum plates used in microelectronics. Ion processing was carried out using an ILM-1 ion implanter equipped with a Pulsar-1M ion source based on a low-pressure glow discharge with a cold hollow cathode. Argon ions with energy of 30 keV and ion current density j = 300 μA/cm2 were used for the irradiation. Two irradiation modes with the fluences of 1016 and 1017 cm–2 were implemented. It was established that the ion treatment promotes the manifestation of the initial grain structure of a sample and increases the mechanical characteristics (modulus of elasticity and nanohardness) of near-surface layers of samples. According to the X-ray diffraction data, after the action of an ion beam, there is a decrease in the size of the coherent scattering region with respect to the initial state. The irradiation leads to an increase in the values of crystal lattice microstrains. Possible mechanisms of modifying the ceramic surface are discussed.

KW - aluminum oxide ceramic (corundum)

KW - ion beams

KW - mechanical characteristics

KW - X-ray phase analysis

UR - http://www.scopus.com/inward/record.url?scp=85066129443&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85066129443&partnerID=8YFLogxK

U2 - 10.1134/S2075113319020199

DO - 10.1134/S2075113319020199

M3 - Article

VL - 10

SP - 438

EP - 444

JO - Inorganic Materials: Applied Research

JF - Inorganic Materials: Applied Research

SN - 2075-1133

IS - 2

ER -