Perspective technologies for production of thermal insulating materials with hard cellular structure

Victor Kutugin, Vasilii Lotov, Yulia Pautova, Antonina Reshetova

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

The method and compositions for the manufacture of foam glass block for single-stage technology, eliminating the annealing stage was developed. The main technological steps are the mixing of the fine-dispersed silica-containing material with additives, granule formation from the mixture, thermal bloating of granules in the metal molds at the temperatures up to 800 °C. The possibility of the extrusion of liquid-glass compositions with simultaneous formation of foam tape was investigated. The obtained materials have a closed and fine-porous structure and enhanced properties - bulk density ρbulk = 150-200 kg/m3 and compressive strength R compr. = 0.5-1.0 MPa. The developed compositions of form-concrete and foam stabilizers allow getting a form-concrete using the synthetic foaming agent on the base of fine sand filler.

Original languageEnglish
Title of host publicationProceedings - 2012 7th International Forum on Strategic Technology, IFOST 2012
DOIs
Publication statusPublished - 2012
Event2012 7th International Forum on Strategic Technology, IFOST 2012 - Tomsk, Russian Federation
Duration: 18 Sep 201221 Sep 2012

Other

Other2012 7th International Forum on Strategic Technology, IFOST 2012
CountryRussian Federation
CityTomsk
Period18.9.1221.9.12

Fingerprint

Thermal insulating materials
Foams
Forms (concrete)
Chemical analysis
Glass
Blowing agents
Molds
Tapes
Compressive strength
Extrusion
Fillers
Sand
Silica
Annealing
Liquids
Metals
Insulating material
Foam
Temperature

Keywords

  • cavitation
  • cellular structure
  • foam concrete
  • foam stabilizer
  • foamglass
  • heat-isolating material
  • liquid-glass

ASJC Scopus subject areas

  • Management of Technology and Innovation

Cite this

Kutugin, V., Lotov, V., Pautova, Y., & Reshetova, A. (2012). Perspective technologies for production of thermal insulating materials with hard cellular structure. In Proceedings - 2012 7th International Forum on Strategic Technology, IFOST 2012 [6357541] https://doi.org/10.1109/IFOST.2012.6357541

Perspective technologies for production of thermal insulating materials with hard cellular structure. / Kutugin, Victor; Lotov, Vasilii; Pautova, Yulia; Reshetova, Antonina.

Proceedings - 2012 7th International Forum on Strategic Technology, IFOST 2012. 2012. 6357541.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Kutugin, V, Lotov, V, Pautova, Y & Reshetova, A 2012, Perspective technologies for production of thermal insulating materials with hard cellular structure. in Proceedings - 2012 7th International Forum on Strategic Technology, IFOST 2012., 6357541, 2012 7th International Forum on Strategic Technology, IFOST 2012, Tomsk, Russian Federation, 18.9.12. https://doi.org/10.1109/IFOST.2012.6357541
Kutugin V, Lotov V, Pautova Y, Reshetova A. Perspective technologies for production of thermal insulating materials with hard cellular structure. In Proceedings - 2012 7th International Forum on Strategic Technology, IFOST 2012. 2012. 6357541 https://doi.org/10.1109/IFOST.2012.6357541
Kutugin, Victor ; Lotov, Vasilii ; Pautova, Yulia ; Reshetova, Antonina. / Perspective technologies for production of thermal insulating materials with hard cellular structure. Proceedings - 2012 7th International Forum on Strategic Technology, IFOST 2012. 2012.
@inproceedings{16b5472208a143f1bc6207063424011e,
title = "Perspective technologies for production of thermal insulating materials with hard cellular structure",
abstract = "The method and compositions for the manufacture of foam glass block for single-stage technology, eliminating the annealing stage was developed. The main technological steps are the mixing of the fine-dispersed silica-containing material with additives, granule formation from the mixture, thermal bloating of granules in the metal molds at the temperatures up to 800 °C. The possibility of the extrusion of liquid-glass compositions with simultaneous formation of foam tape was investigated. The obtained materials have a closed and fine-porous structure and enhanced properties - bulk density ρbulk = 150-200 kg/m3 and compressive strength R compr. = 0.5-1.0 MPa. The developed compositions of form-concrete and foam stabilizers allow getting a form-concrete using the synthetic foaming agent on the base of fine sand filler.",
keywords = "cavitation, cellular structure, foam concrete, foam stabilizer, foamglass, heat-isolating material, liquid-glass",
author = "Victor Kutugin and Vasilii Lotov and Yulia Pautova and Antonina Reshetova",
year = "2012",
doi = "10.1109/IFOST.2012.6357541",
language = "English",
isbn = "9781467317702",
booktitle = "Proceedings - 2012 7th International Forum on Strategic Technology, IFOST 2012",

}

TY - GEN

T1 - Perspective technologies for production of thermal insulating materials with hard cellular structure

AU - Kutugin, Victor

AU - Lotov, Vasilii

AU - Pautova, Yulia

AU - Reshetova, Antonina

PY - 2012

Y1 - 2012

N2 - The method and compositions for the manufacture of foam glass block for single-stage technology, eliminating the annealing stage was developed. The main technological steps are the mixing of the fine-dispersed silica-containing material with additives, granule formation from the mixture, thermal bloating of granules in the metal molds at the temperatures up to 800 °C. The possibility of the extrusion of liquid-glass compositions with simultaneous formation of foam tape was investigated. The obtained materials have a closed and fine-porous structure and enhanced properties - bulk density ρbulk = 150-200 kg/m3 and compressive strength R compr. = 0.5-1.0 MPa. The developed compositions of form-concrete and foam stabilizers allow getting a form-concrete using the synthetic foaming agent on the base of fine sand filler.

AB - The method and compositions for the manufacture of foam glass block for single-stage technology, eliminating the annealing stage was developed. The main technological steps are the mixing of the fine-dispersed silica-containing material with additives, granule formation from the mixture, thermal bloating of granules in the metal molds at the temperatures up to 800 °C. The possibility of the extrusion of liquid-glass compositions with simultaneous formation of foam tape was investigated. The obtained materials have a closed and fine-porous structure and enhanced properties - bulk density ρbulk = 150-200 kg/m3 and compressive strength R compr. = 0.5-1.0 MPa. The developed compositions of form-concrete and foam stabilizers allow getting a form-concrete using the synthetic foaming agent on the base of fine sand filler.

KW - cavitation

KW - cellular structure

KW - foam concrete

KW - foam stabilizer

KW - foamglass

KW - heat-isolating material

KW - liquid-glass

UR - http://www.scopus.com/inward/record.url?scp=84871828652&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84871828652&partnerID=8YFLogxK

U2 - 10.1109/IFOST.2012.6357541

DO - 10.1109/IFOST.2012.6357541

M3 - Conference contribution

AN - SCOPUS:84871828652

SN - 9781467317702

BT - Proceedings - 2012 7th International Forum on Strategic Technology, IFOST 2012

ER -