Obtained Heteromodulus Composites Based on Zirconium Carbide

Yu A. Mirovoy, A. G. Burlachenko, S. P. Buyakova, S. N. Kulkov

Research output: Contribution to journalConference article

Abstract

The article is devoted to the impact of carbon additives on densification and mechanical properties of ZrC/C heteromodulus composites. In case of addition of small amount of carbon to ZrC residual porosity decreases, whereas higher carbon content leads to more than 3vol.% increase in residual porosity. Moreover, increase in carbon content in ZrC/C composites boosts toughness of sintered materials. For example, IC =4.3 MPa×m1/2 for ZrC and IC =7 MPa×m1/2. for 3 vol.% C. For 15 vol.% of C, toughness is the lowest and equals 5.3 MPa×m1/2. The extrapolation of the dependence of toughness on the non-porous state of materials is IC0 =13.2 MPa×m1/2.

Original languageEnglish
Article number012010
JournalIOP Conference Series: Materials Science and Engineering
Volume696
Issue number1
DOIs
Publication statusPublished - 27 Nov 2019
Event3rd International Scientific and Technical Conference on Materials, Technology and Equipment for the Development of the Arctic and Siberia, ARCTIC 2019 - Tomsk, Russian Federation
Duration: 25 Sep 201928 Sep 2019

    Fingerprint

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

Cite this