Long-term operation of rail steel: Degradation of structure and properties of surface layer

V. E. Gromov, Yu F. Ivanov, K. V. Morozov, O. A. Peregudov, O. A. Semina

Research output: Contribution to journalArticle

6 Citations (Scopus)

Abstract

By methods of optical, scanning and transmission electron diffraction microscopy and microhardness and tribology parameters measurement the changes regularities of structure-phase states, defect substructure of rails surface after the long term operation (passed tonnage of gross weight 500 and 1000 mln. tons) were established. It is shown that the wear rate increases in 3 and 3.4 times after passed tonnage of gross weight 500 and 1000 mln. tons, accordingly, and the friction coefficient decreases in 1.4 and 1.1 times. The cementite plates are destroying absolutely and cementite particles of around form with the sizes 10–50 nm are forming after passed tonnage 500 mln tons. The appearance of dynamical recrystallization initial stages is marked after the passed tonnage 1000 mln tons. The possible mechanisms of established regularities are discussed. It is noted that two competitive processes can take place during rails long term operation: 1. Process of cutting of cementite particles followed by their carrying out into the volume of ferrite grains or plates (in the structure of pearlite). 2. Process of cutting, the subsequent dissolution of cementite particles, transition of carbon atoms to dislocations (into Cottrell atmospheres), transition of carbon atoms by dislocations into volume of ferrite grains or plates followed by repeat formation of nanosize cementite particles.

Original languageEnglish
Pages (from-to)1101-1105
Number of pages5
JournalJournal of Surface Investigation
Volume10
Issue number5
DOIs
Publication statusPublished - 1 Sep 2016

Fingerprint

Steel
Ferrite
Rails
Carbon
Degradation
Atoms
Pearlite
Tribology
Phase structure
Light transmission
Electron diffraction
Microhardness
Microscopic examination
Dissolution
Wear of materials
Friction
Scanning
Defects

Keywords

  • defect substructure
  • operation
  • phase composition
  • rails
  • structure
  • surface layer

ASJC Scopus subject areas

  • Surfaces, Coatings and Films

Cite this

Long-term operation of rail steel : Degradation of structure and properties of surface layer. / Gromov, V. E.; Ivanov, Yu F.; Morozov, K. V.; Peregudov, O. A.; Semina, O. A.

In: Journal of Surface Investigation, Vol. 10, No. 5, 01.09.2016, p. 1101-1105.

Research output: Contribution to journalArticle

Gromov, V. E. ; Ivanov, Yu F. ; Morozov, K. V. ; Peregudov, O. A. ; Semina, O. A. / Long-term operation of rail steel : Degradation of structure and properties of surface layer. In: Journal of Surface Investigation. 2016 ; Vol. 10, No. 5. pp. 1101-1105.
@article{e656786de9e54c19aa29c64861ca78c2,
title = "Long-term operation of rail steel: Degradation of structure and properties of surface layer",
abstract = "By methods of optical, scanning and transmission electron diffraction microscopy and microhardness and tribology parameters measurement the changes regularities of structure-phase states, defect substructure of rails surface after the long term operation (passed tonnage of gross weight 500 and 1000 mln. tons) were established. It is shown that the wear rate increases in 3 and 3.4 times after passed tonnage of gross weight 500 and 1000 mln. tons, accordingly, and the friction coefficient decreases in 1.4 and 1.1 times. The cementite plates are destroying absolutely and cementite particles of around form with the sizes 10–50 nm are forming after passed tonnage 500 mln tons. The appearance of dynamical recrystallization initial stages is marked after the passed tonnage 1000 mln tons. The possible mechanisms of established regularities are discussed. It is noted that two competitive processes can take place during rails long term operation: 1. Process of cutting of cementite particles followed by their carrying out into the volume of ferrite grains or plates (in the structure of pearlite). 2. Process of cutting, the subsequent dissolution of cementite particles, transition of carbon atoms to dislocations (into Cottrell atmospheres), transition of carbon atoms by dislocations into volume of ferrite grains or plates followed by repeat formation of nanosize cementite particles.",
keywords = "defect substructure, operation, phase composition, rails, structure, surface layer",
author = "Gromov, {V. E.} and Ivanov, {Yu F.} and Morozov, {K. V.} and Peregudov, {O. A.} and Semina, {O. A.}",
year = "2016",
month = "9",
day = "1",
doi = "10.1134/S1027451016050281",
language = "English",
volume = "10",
pages = "1101--1105",
journal = "Journal of Surface Investigation",
issn = "1027-4510",
publisher = "Maik Nauka-Interperiodica Publishing",
number = "5",

}

TY - JOUR

T1 - Long-term operation of rail steel

T2 - Degradation of structure and properties of surface layer

AU - Gromov, V. E.

AU - Ivanov, Yu F.

AU - Morozov, K. V.

AU - Peregudov, O. A.

AU - Semina, O. A.

PY - 2016/9/1

Y1 - 2016/9/1

N2 - By methods of optical, scanning and transmission electron diffraction microscopy and microhardness and tribology parameters measurement the changes regularities of structure-phase states, defect substructure of rails surface after the long term operation (passed tonnage of gross weight 500 and 1000 mln. tons) were established. It is shown that the wear rate increases in 3 and 3.4 times after passed tonnage of gross weight 500 and 1000 mln. tons, accordingly, and the friction coefficient decreases in 1.4 and 1.1 times. The cementite plates are destroying absolutely and cementite particles of around form with the sizes 10–50 nm are forming after passed tonnage 500 mln tons. The appearance of dynamical recrystallization initial stages is marked after the passed tonnage 1000 mln tons. The possible mechanisms of established regularities are discussed. It is noted that two competitive processes can take place during rails long term operation: 1. Process of cutting of cementite particles followed by their carrying out into the volume of ferrite grains or plates (in the structure of pearlite). 2. Process of cutting, the subsequent dissolution of cementite particles, transition of carbon atoms to dislocations (into Cottrell atmospheres), transition of carbon atoms by dislocations into volume of ferrite grains or plates followed by repeat formation of nanosize cementite particles.

AB - By methods of optical, scanning and transmission electron diffraction microscopy and microhardness and tribology parameters measurement the changes regularities of structure-phase states, defect substructure of rails surface after the long term operation (passed tonnage of gross weight 500 and 1000 mln. tons) were established. It is shown that the wear rate increases in 3 and 3.4 times after passed tonnage of gross weight 500 and 1000 mln. tons, accordingly, and the friction coefficient decreases in 1.4 and 1.1 times. The cementite plates are destroying absolutely and cementite particles of around form with the sizes 10–50 nm are forming after passed tonnage 500 mln tons. The appearance of dynamical recrystallization initial stages is marked after the passed tonnage 1000 mln tons. The possible mechanisms of established regularities are discussed. It is noted that two competitive processes can take place during rails long term operation: 1. Process of cutting of cementite particles followed by their carrying out into the volume of ferrite grains or plates (in the structure of pearlite). 2. Process of cutting, the subsequent dissolution of cementite particles, transition of carbon atoms to dislocations (into Cottrell atmospheres), transition of carbon atoms by dislocations into volume of ferrite grains or plates followed by repeat formation of nanosize cementite particles.

KW - defect substructure

KW - operation

KW - phase composition

KW - rails

KW - structure

KW - surface layer

UR - http://www.scopus.com/inward/record.url?scp=84991786883&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84991786883&partnerID=8YFLogxK

U2 - 10.1134/S1027451016050281

DO - 10.1134/S1027451016050281

M3 - Article

AN - SCOPUS:84991786883

VL - 10

SP - 1101

EP - 1105

JO - Journal of Surface Investigation

JF - Journal of Surface Investigation

SN - 1027-4510

IS - 5

ER -