Abstract
Neutron-diffraction analysis and measurements of electrical resistance were used to investigate the kinetics of ordering in Ni3(Mn, Cu) alloys preliminarily tempered at 900°C, containing 0.45-9.29 at.% copper. It was established that introducing copper atoms in place of manganese atoms in the alloy Ni3Mn leads to slowing of the ordering process. The degree of long-range order inside antiphase domains in Ni3(Mn, Cu) alloys is less than in the binary alloy.
| Original language | English |
|---|---|
| Pages (from-to) | 306-309 |
| Number of pages | 4 |
| Journal | Soviet Physics Journal |
| Volume | 20 |
| Issue number | 3 |
| DOIs | |
| Publication status | Published - Mar 1977 |
Fingerprint
ASJC Scopus subject areas
- Physics and Astronomy(all)
- Engineering(all)
Cite this
Kinetics of ordering in Ni3Mn alloy with additions of copper. / Lotkov, A. I.; Panin, V. E.; Fadin, V. P.
In: Soviet Physics Journal, Vol. 20, No. 3, 03.1977, p. 306-309.Research output: Contribution to journal › Article
}
TY - JOUR
T1 - Kinetics of ordering in Ni3Mn alloy with additions of copper
AU - Lotkov, A. I.
AU - Panin, V. E.
AU - Fadin, V. P.
PY - 1977/3
Y1 - 1977/3
N2 - Neutron-diffraction analysis and measurements of electrical resistance were used to investigate the kinetics of ordering in Ni3(Mn, Cu) alloys preliminarily tempered at 900°C, containing 0.45-9.29 at.% copper. It was established that introducing copper atoms in place of manganese atoms in the alloy Ni3Mn leads to slowing of the ordering process. The degree of long-range order inside antiphase domains in Ni3(Mn, Cu) alloys is less than in the binary alloy.
AB - Neutron-diffraction analysis and measurements of electrical resistance were used to investigate the kinetics of ordering in Ni3(Mn, Cu) alloys preliminarily tempered at 900°C, containing 0.45-9.29 at.% copper. It was established that introducing copper atoms in place of manganese atoms in the alloy Ni3Mn leads to slowing of the ordering process. The degree of long-range order inside antiphase domains in Ni3(Mn, Cu) alloys is less than in the binary alloy.
UR - http://www.scopus.com/inward/record.url?scp=0017462981&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0017462981&partnerID=8YFLogxK
U2 - 10.1007/BF00894835
DO - 10.1007/BF00894835
M3 - Article
AN - SCOPUS:0017462981
VL - 20
SP - 306
EP - 309
JO - Russian Physics Journal
JF - Russian Physics Journal
SN - 1064-8887
IS - 3
ER -