TY - JOUR
T1 - Features of chemical-mineralogical composition and processing properties for medium-ferrous bauxites
AU - Govorova, L. P.
AU - Vakalova, T. V.
AU - Shvagrukova, E. V.
AU - Reshetova, A. A.
AU - Potapova, A. P.
N1 - Publisher Copyright:
© The Authors, published by EDP Sciences, 2016.
Copyright:
Copyright 2017 Elsevier B.V., All rights reserved.
PY - 2016/11/17
Y1 - 2016/11/17
N2 - The features of chemical-mineralogical composition and processing properties of bauxites from Iksinsk and Severoonezhsk deposits are investigated in the paper. It is found that the studied bauxites are coarsely dispersed and low-dispersive, high-Alumina clay raw materials with a high content of colouring oxides. According to their mineralogical composition, Iksinsk and Severoonezhsk bauxites are boehmite-hydrargillite-kaolinite clay bauxites. Moreover, Iksinsk bauxite samples are characterized by the total absence of quartz impurities. The samples of plastic molding based on Iksinsk bauxites are fully sintered at 1500 °C with the formation of strong structures with a compressive strength of 70-120 MPa (depending on the variety of bauxites). The samples based on Severoonezhsk bauxites are fully sintered at 1450 °C, and they are characterized by a compressive strength to 70 MPa in the sintered state.
AB - The features of chemical-mineralogical composition and processing properties of bauxites from Iksinsk and Severoonezhsk deposits are investigated in the paper. It is found that the studied bauxites are coarsely dispersed and low-dispersive, high-Alumina clay raw materials with a high content of colouring oxides. According to their mineralogical composition, Iksinsk and Severoonezhsk bauxites are boehmite-hydrargillite-kaolinite clay bauxites. Moreover, Iksinsk bauxite samples are characterized by the total absence of quartz impurities. The samples of plastic molding based on Iksinsk bauxites are fully sintered at 1500 °C with the formation of strong structures with a compressive strength of 70-120 MPa (depending on the variety of bauxites). The samples based on Severoonezhsk bauxites are fully sintered at 1450 °C, and they are characterized by a compressive strength to 70 MPa in the sintered state.
UR - http://www.scopus.com/inward/record.url?scp=85008429737&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85008429737&partnerID=8YFLogxK
U2 - 10.1051/matecconf/20168501025
DO - 10.1051/matecconf/20168501025
M3 - Conference article
AN - SCOPUS:85008429737
VL - 85
JO - MATEC Web of Conferences
JF - MATEC Web of Conferences
SN - 2261-236X
M1 - 01025
T2 - Chemistry and Chemical Technology in XXI Century, CCT 2016
Y2 - 17 May 2016 through 20 May 2016
ER -